Epomarine PC 100
PRODUCT DESCRIPTION
& INTENDED USES
產品簡介
FEATURES
產品特性 |
|
環氧涂料 PC 100
A high-build epoxy paint for interior surfaces of steel cans where
chemical, solvent and salt water resistance are required.
厚涂型環氧涂料，用于有耐化、耐溶劑、耐鹽水要求的鋼結構儲罐
內面。 |
|
| |
z Remarkable resistance to crude oil, petroleum products, aliphatic
solvents, salt water and a broad range of chemicals
良好的耐原油、石油、脂肪烴溶劑性能和耐鹽水性，同時對多
種化學藥品有良好的耐受性
z Excellent high-build applicability
極好的厚涂施工性能
z Excellent anti-abrasion and impact-resistant properties
極好的耐磨損和耐沖擊性能
|
|
BASIC DATA
基本數據
Color(s)
顏色
Mixing ratio
混合比率
Solid content
重量固體份
Film
thickness
涂裝膜厚
Spreading
rate
涂覆率 |
|
White and Pink
白色、粉紅色
Base/Hardener=70/10 (by wt.)
主劑/固化劑=70/10（重量比）
70 |
Dry : 75-
150microns/coat
干膜: 75-150mm/道
|
Wet : 150-319 microns/coat
濕膜: 150-319mm/道 |
|
Theoretical: 0.305kg/m 2/125 microns
理論值 : 0.305 千克/平方米/125mm
Practical: Various depending on surface conditions, environment,
applications, etc.
實際值 : 與表面處理, 外界環境, 施工方法等多種因素有關。 |
|
STORAGE
儲存
Shelf temperature
儲存溫度
Shelf life
儲存期限
Flash point
閃點
APPLICATION DATA
施工數據
Pot life
混合使用期
|
|
0℃-40℃
1 year
1 年
Greater than
27℃
27℃以上 |
|
| |
Temperature (℃)溫度
Pot life (hrs) 混合使用期 |
|
|
|
|
|
|
|
| |
Airless spray, air spray, brush and
roller
無氣噴涂、空氣噴涂、刷涂及輥涂 |
Airless
spray
Nozzle tip
Fluid
pressure
Thinning
|
|
Recommended 推薦
0.021-0.023
100-150kg/cm
0-5% by volume（體積比）
|
|
|
Thinner
稀釋劑
Application
temperature
施工溫度
Drying time &
Overcoating int
erval
干燥時間&涂裝間隔 |
|
Epomarine Thinner 80
環氧稀釋劑 80
5℃-40℃
|
|
| |
Temperature (℃)
Dry to touch (hrs)
Dry hard (hrs)
Full cure (weeks)
Min. interval (hrs)
Max. interval (days) |
溫度
指觸干燥
半硬干燥
完全干燥
最小涂裝間隔
最大涂裝間隔 |
|
|
|
|
|
|
PAINTING SYSTEM
涂裝配套
Applied substrates
適用底材
Preceding coat
適用下涂
SURFACE
PREPARATION
表面處理 |
|
Bare steel.
裸鋼。
Epomarine Primer PC or according to the coating systems by Kansai
Epomarine primer PC，或參考我司推薦配套。 |
|
| |
z Remove salt and other water-soluble contaminants by fresh water
hosing.
用清水沖去鹽份及其它水溶性污物。
z Degrease according to SSPC-SP1 solvent cleaning.
依照 SSPC-SP1 溶劑清洗標準除去油脂。
z Remove weld spatter and smooth weld seams and sharp edges.
除去焊接飛濺并處理焊縫、毛刺使其光順。
z Remove rust, mill-scale and damaged shop primer by blasting to
near white metal ISO Sa2.5 (SSPC-SP10) or better.
用噴砂方式除去鐵銹、氧化皮和損壞的車間底漆達到 ISO Sa2.5
(SSPC-SP10)或更好。
z Remove dust and dirt by high-pressure air before paint application
用高壓空氣吹掃除去灰塵等污物。
z Be sure that the surface is clean and dry prior to application.
施工前確認表面清潔干燥。 |
|